anti pid series eva film
f406p&f806p
product introduction
the potential induced degradation (pid) within the system of a solar module may cause severe power loss of pv system. f•rst® f406p&f806p eva provides an encapsulant solution for a pid-free requirement of the pv module. f•rst® f406p&f806p eva provides excellent pid-resistance which can withstand 96h pid testing under conditions of 85℃, rh 85%, -1000vdc. the p-series eva also exhibits excellent durability and high transmittance.
anti pid property (85℃,85%rh,-1000vdc)
glass f406p eva silicon cell f806p eva bec301 backsheet
initial(251.2w) pid96h(250.6w)
performance parameter
| properties | test method | units | f406p | f806p | |
| general gram weight | fst method | g/m2 | 430±20 | 390±20 | |
| thickness | fst method | mm | 0.55±0.05 | 0.50±0.05 | |
| length | fst method | m/roll | 150 | 150 | |
| width | fst method | mm | customization0/ 7 | customization0/ 7 | |
| density | astmd792 | g/cm3 | 0.95-0.96 | 0.95-0.96 | |
| melting range | fst method | ℃ | 40-80 | 40-80 | |
| shrinkage rate(120℃,3min) | gb/t29848 | md% | <3.0 | <3.0 | |
| td% | <1.5 | <1.5 | |||
| uv-cutoff wavelength | fst method | nm | -- | 360 | |
| transmittance | 1100nm-380nm | gb/t29848 | % | >91 | >91 |
| 380nm-290nm | % | >80 | <30 | ||
| gel content | gb/t29848 | gel% | >75 | >75 | |
| volume resistivity | gb/t29848 | ω·cm | >1.0×1015 | >1.0×1015 | |
| strength of peeling from glass | gb/t29848 | n/cm | >60 | >60 | |
| strength of peeling from tpt | gb/t29848 | n/cm | >40 | >40 | |